Title: Caracterização de aços maraging livres de cobalto produzidos por metalurgia do pó
metadata.dc.creator: Pereira, Eduardo Emanuel de Lima
metadata.dc.contributor.advisor1: Silva Júnior, Manoel Quirino da
metadata.dc.contributor.referee1: Fraga, Francisco Edson Nogueira
metadata.dc.contributor.referee2: Reis, Francisco Evaristo Uchoa
metadata.dc.description.resumo: Os aços maraging são materiais muito importantes e relevantes como alternativas para as mais diversas aplicações devido a sua junção de propriedades desejadas. Entretanto não são materiais baratos, e buscam-se alternativas para facilitar sua obtenção. O presente trabalho tem por objetivo a obtenção e caracterização de uma série de aços maraging, e para isso, analisou amostras de três tipos de aços maraging diferentes pertencentes à série T, sendo eles T-200, T-250 e T-300, que foram produzidas por metalurgia do pó. Foram utilizadas técnicas para a caracterização dessas amostras, sendo elas a microscopia, o ensaio de micro dureza e a difração de raios-x. Os resultados obtidos mostraram como a pressão de compactação e a temperatura de sinterização influenciaram no nível de porosidade das amostras, bem como na dureza média delas. Já a difração de raios-x mostrou que os difratogramas das amostras foram muito parecidos, quase idênticos.
Abstract: Maraging steels are very important and relevant materials as alternatives for the most diverse applications due to their combination of desired properties. However they are not cheap materials, and alternatives are sought to facilitate their obtaining. The aim of the present work was to obtain and characterize a series of maraging steels, and for that, analyzed samples of three types of different maraging steels belonging to the T series, being T-200, T-250 and T-300, which were produced by powder metallurgy. Techniques were used to characterize these samples, such as microscopy, microhardness test and x-ray diffraction. The results showed how the compression pressure and the sintering temperature influenced the porosity of the samples as well as their average hardness. The X-ray diffraction showed that the diffractograms of the samples were very similar, almost identical.
Keywords: Aços Maraging
Caracterização
Propriedades
Maraging Steel
Characterize
Maraging Steel, Properties
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal Rural do Semi-Árido
metadata.dc.publisher.initials: UFERSA
metadata.dc.publisher.department: Centro de Engenharias - CE
Citation: Pereira (2019) (PEREIRA, 2019)
metadata.dc.rights: Acesso Aberto
URI: http://repositorio.ufersa.edu.br/handle/prefix/1496
http://repositorio.ufersa.edu.br/handle/prefix/3648
Issue Date: 27-Mar-2019
Appears in Collections:Engenharia Mecânica

Files in This Item:
File Description SizeFormat 
EduardoELP_MONO.pdf2.35 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.