Title: Caracterização das morfologias encontradas no metal de solda variando a energia de soldagem
metadata.dc.creator: Borges, Igor Vinícios de Lima
metadata.dc.contributor.advisor1: Reis, Francisco Evaristo Uchoa
metadata.dc.contributor.referee1: Fraga, Francisco Edson Nogueira
metadata.dc.contributor.referee2: Lima, Ramsés Otto Cunha de
metadata.dc.description.resumo: O estudo da importância dos parâmetros da soldagem sobre a microestrutura dos materiais metálicos é de grande importância pois a avaliação dos microconstituintes tem relação direta com as propriedades mecânicas finais obtidas na junta soldada, assim como a morfologia do grão que desempenha um papel importante na tenacidade do metal de solda. Algumas variáveis no processo de soldagem podem influenciar na solidificação do metal de solda, como por exemplo a energia de soldagem, a espessura do material, a condutividade térmica do material e o pré-aquecimento, em que todas estão associadas à taxa de resfriamento que, por sua vez, influencia diretamente nos processos de nucleação e crescimento na solidificação. O presente trabalho tem o objetivo de identificar diferentes morfologias de grão que podem ser encontradas em um metal de solda em função da variação da energia de soldagem. Dessa forma, foram realizados experimentos com solda TIG autógena variando a corrente de soldagem, consequentemente variava a energia de soldagem em dois níveis 157,51 J/cm e 272,02 J/cm (soldagem à 100A e 150A), mantendo a temperatura ambiente e demais parâmetros constantes. Os metais de solda foram analisados metalograficamente, caracterizando as morfologias de grão presentes nas seções transversais dos cordões de solda. Foram encontradas combinações de morfologias distintas para cada energia de soldagem. Na amostra na qual foi utilizada a corrente de 100 ampères foi observada uma zona colunar seguida por uma equiaxial central, além da ausência de uma zona coquilhada e na amostra de 150 ampères apresentou juntamente com as morfologias encontradas na amostra de 100A um pouco de crescimento epitaxial, revelando a influência da energia de soldagem. Suplementarmente foi possível constatar que a largura e a profundidade do cordão de solda aumentam conforme o parâmetro é aumentado.
Abstract: The study of the importance of the welding parameters on the microstructure of the metallic materials is of great importance since the evaluation of the microconstituents has a direct relation with the final mechanical properties obtained in the welded joint, as well as the grain morphology that plays an important role in the toughness of the welding metal. Some variables in the welding process may influence the solidification of the weld metal, such as welding energy, material thickness, material thermal conductivity and preheating, that the two parties contain cooling rates which, in turn, directly influences the processes of nucleation and growth in solidification. The present work has the objective of identifying different grain morphologies that can be found in a weld metal as a depending on the variation of the welding energy. Thus, experiments with autogenous TIG welding were performed, varying the welding current, whereby the welding energy varied in two levels, 157.51 J / cm and 272.02 J / cm (welding at 100A and 150A), maintaining the temperature environment and other constant parameters. The weld metals were analyzed by metallography, characterizing the grain morphologies present in the cross sections of the weld beads. Combinations of different morphologies were found for each welding energy. In the sample in which the current of 100 A was used, a columnar zone followed by a central equiaxial was observed, besides the absence of a quenched zone and in the sample of 150 A presented along with the morphologies found in the 100A sample a little epitaxial growth , revealing the influence of welding energy. In addition, it was possible to verify that the width and depth of the weld bead increase as the parameter is increased.
Keywords: Metal de solda
TIG autógeno
Microestrutura
Solidificação
Parâmetros de soldagem
Welding Metal
Autogenous TIG
Solidification
Welding Parameters
Microstructure
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal Rural do Semi-Árido
metadata.dc.publisher.initials: UFERSA
metadata.dc.publisher.department: Centro de Engenharias - CE
Citation: Borges (2019) (BORGES, 2019)
metadata.dc.rights: Acesso Aberto
URI: http://repositorio.ufersa.edu.br/handle/prefix/1500
http://repositorio.ufersa.edu.br/handle/prefix/3655
Issue Date: 12-Mar-2019
Appears in Collections:Engenharia Mecânica

Files in This Item:
File Description SizeFormat 
IgorVLB_MONO.pdf1.2 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.