Title: Caracterização microestrutural de uma liga do sistema Cu-Al-Mn com memória de forma
metadata.dc.creator: Alves, Jéssica Menezes
metadata.dc.contributor.advisor1: Alcântara, Carlos Cássio de
metadata.dc.contributor.referee1: Guimarães, Aracelle de Albuquerque Santos
metadata.dc.contributor.referee2: Nascimento, Joe Vitor Alves do
metadata.dc.description.resumo: Neste trabalho foi feito a caracterização microestrutural de uma liga do sistema Cu-Al-Mn passível de efeito memoria de forma. As ligas foram elaboradas em forno sob atmosfera ambiente, tratadas termicamente por homogeinização e têmpera, foram feitos corpos de prova e então caracterizadas por ensaios de microscopia óptica, difração de raios-x, e tração. Percebeu-se que a temperatura ambiente a liga bruta apresenta as fases β, γ e Al8Mn5. Após a têmpera apresentou a fase Autenítica β, quando resfriado apresentou a fase Martensítica indicando o efeito memoria de forma confirmando ser uma liga de características superelástica. A amostra tracionada exibiu fases martensiticas e outras que foram determinadas com o auxílio do DRX. No ensaio por DRX foi possível determinar a fases da liga, na amostra bruta de fusão é possível identificar a fase β, de estrutura L21 e grupo espacial Fm3m, a fase γ, que apresenta estrutura Cu9Al4 e grupo espacial P-43mn e uma terceira fase, identificada sob a forma de Al8Mn5, de estrutura CCC e grupo espacial I 43m. Na amostra Temperada é possível notar a supressão das fases existentes na amostra bruta de fusão após a têmpera. A amostra exibe apenas a fase austenítica β, de estrutura L21 e grupo espacial Fm3m. A amostra tracionada exibiu a fase β, a fase γ de plano e a fase martensítica ortorrômbica γ’, de fórmula estrutural AlCu3 e grupo espacial P2mm, que representa uma das duas fases martensíticas que podem ser formadas em ligas CuAlMn.
Abstract: In this work, the microstructural characterization of an alloy of the Cu-Al-Mn system was carried out. The alloys were oven-worked under ambient atmosphere, heat-treated by homogenization and quenching, specimens were made and then characterized by optical microscopy, x-ray diffraction, and tensile tests. It was noticed that at room temperature the crude alloy presents the phases β, γ and Al8Mn5. After the tempering presented the Autentic phase β, when cooled presented the Martensitic phase indicating the shape memory effect confirming to be an alloy of superelastic characteristics. The drawn sample exhibited martensitic phases and others that were determined with the aid of XRD. In the XRD test, it was possible to determine the alloy phases. In the crude fusion sample, it is possible to identify the phase β of structure L21 and space group Fm3m, phase γ, which presents structure Cu9Al4 and space group P-43mn and a third phase , identified in the form of Al8 Mn5, CCC structure and space group I 43m. In the Temperate sample, it is possible to observe the suppression of the existing phases in the crude melt sample after tempering. The sample shows only the austenitic phase β, structure L21 and space group Fm3m. The drawn sample showed the β phase, the plane γ phase and the orthorhombic γ 'martensitic phase of the AlCu3 structural formula and the P2mm spatial group, which represents one of the two martensitic phases that can be formed in CuAlMn alloys.
Keywords: Efeito memória de forma
Ligas superelásticas
Ligas de CuAlMn
DRX
metadata.dc.subject.cnpq: CNPQ::CIENCIAS EXATAS E DA TERRA
metadata.dc.language: por
metadata.dc.publisher.country: Brasil
Publisher: Universidade Federal Rural do Semi-Árido
metadata.dc.publisher.initials: UFERSA
metadata.dc.publisher.department: Centro Multidisciplinar de Caraúbas
Citation: Alves (2018) (ALVES, 2018)
metadata.dc.rights: Acesso Aberto
URI: http://repositorio.ufersa.edu.br/handle/prefix/2130
http://repositorio.ufersa.edu.br/handle/prefix/3051
Issue Date: 17-Sep-2018
Appears in Collections:Engenharia Mecânica

Files in This Item:
File Description SizeFormat 
JÉSSICAMA_MONO.pdf1.3 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.